SynTherm® – Insulating Materials SynTherm® YT510 (metastar® YT510)

SynTherm® YT510 is a synthetic electro-insulation paper constructed of a calandered, aromatic polyamide fibride flock composition.

SynTherm® YT510 is a Class H (180 °C) insulating material. Temperatures below 200 °C only slightly influence its electrical properties. The excellent mechanical properties can be extrapolated at much higher temperatures. Due to the polymer structure, SynTherm® YT510 can also be used at temperatures as low as -190 °C.

It has a high short-time field intensity. SynTherm® YT510 is compatible with all common resin, varnish, adhesive classes, as well as transformer liquids, oils and refrigerants. Common solvents can result in easily reversible expansion. SynTherm® YT510 paper is flame resistant (UL 94V-0), moreover, it displays a very high level of beta and gamma-ray resistance.

Download datasheet

Application

High quality SynTherm® YT510 is used in almost all known applications for electrical insulating materials. Application ranges from AC and DC motors to large generators, wet and dry transformers and chokes, even with beta and gamma radiation exposure.

Standards

  • Class H (180 °C) insulating material
  • UL approved (RTI 210 °C)
  • UL file no. E358562

Delivery forms

Film thickness in µm:
50, 80, 130, 180, 250, 300, 380, 510, 760

SYNTHERM® YT510 can be supplied:

  • in slit rolls: Depending on the material thickness
  • in rolls: 1000 mm


Feathering:

  • depth approx. 1 - 12 mm, distance approx. 1 - 10 mm
  • from widths of 10 to 240 mm and thickness of 0.25 mm

Base

Calandered, aromatic polyamide fibride flock composition

Punched parts, bent & formed parts

We offer a wide range of punched and formed parts: Rolls, individual parts unsorted, sorted or stacked, adhesive on one or both sides, non-adhesive, with or without a grip tab.

 

More about punched parts

Technical data

Mechanical
Property Unit of measure Test method
Nominal thickness μm 50 80 130 180 250 300 380 510 760
Typical thickness µm 55 78 130 180 245 290 365 515 755 GB/T451.3-2002
Specific weight g/m² 41 63 116 175 249 309 390 510 690 GB/T451.2-2002
Tensile strength longitudinal N/cm 39 66 140 220 255 320 380 500 650 GB/T12914-2008
Tensile strength transversal N/cm 15 29 56 105 165 200 260 345 450 GB/T12914-2008
Elongation at break longitudinal % 7 8.5 10 11 13.5 16 13 13 13 GB/T12914-2008
Elongation at break transversal % 6.5 9 11.5 12.5 14.5 15.5 12 13 12 GB/T12914-2008
Shrinkage at 300 °C longitudinal % 3.5 3.5 3.0 3.0 3.0 3.0 3.0 3.0 3.0 IEC60819-2:2002
Shrinkage at 300 °C transversal % 3.0 3.0 2.5 2.5 2.5 2.5 2.5 2.0 2.0 IEC60819-2:2002
Elmendorf tear strength longitudinal N 0.65 1.0 2.0 3.5 5.0 6.5 10 13 - GB/T455-2002
Elmendorf tear strength transversal N 1.15 1.7 3.3 4.8 6.0 8.0 13.5 16 - GB/T455-2002
Electrical
Property Unit of measure Test method
Nominal thickness μm 50 80 130 180 250 300 380 510 760
Field intensity kV/mm 13 14 18 20 22 23 20 18 19 GB/T1408.1-2006
Dielectric constant (50 Hz) 1.5 1.5 2.1 2.4 2.5 2.7 3.0 3.1 3.2 GB/T1409-2006