Winding wire SHTherm® 210 Flat Alu
- Enamelled flat aluminium wire, thermoresistant
- insulated with THEIC mod. polyesterimide with polyamide-imide topcoat
- Class 200
SHTherm® 210 Flat Alu is a highly thermoresistant rectangular enamelled aluminium wire of heat performance class N with a wide range of good to very good quality features. Its insulation film consists of 2 different coatings on top of one another. These ensure a very good permanent thermal and overload resistance, excellent resistance against mechanical stress, as well as an excellent resistance to chemical attacks of commercial washing and cleaning agents, impregnating varnishes and resins, sealing compounds, thinners, solvents and refrigerants, oils as well as their vapours. This range of excellent features make SHTherm® 210 Flat Alu an all-round wire meeting the requirements of all applications with above average requirements to processing and operational features or operational safety in electrical systems.
Application
Generators, transformers
Standards
IEC / DIN EN 60317-73
NEMA MW 36-A
UL approved
Delivery forms
Grade 1: on request
Grad 2: on request
Technical data
Typical properties of enamelled flat aluminium wire 5.60 x 3.55 mm, with insulation film grade 2
| Property | Unit of measure | Set value | Actual value (typ.) |
|---|---|---|---|
| Bare wire width | mm | 5.550-5.650 | as set value |
| Bare wire thickness | mm | 3.500-3.600 | as set value |
| Width with varnish | mm | 5.67 - 5.82 | as set value |
| Thickness with varnish | mm | 3.62 - 3.77 | as set value |
| Varnish increase | μm | 120 - 170 μm | as set value |
| Adhesion (no cracks in film after winding) | mandrel diamter | mandrel diameter | |
| Bend over width | 4 x width | 3 x width | |
| Bend over thickness | 4 x thickness | 3 x thickness | |
| Elongation | 15 % with cracks < 1 x width | 32 % without cracks | |
| Pencil hardness | H | 4H - 5H | |
| Elongation at break | % | ≥ 15 | ≥ 32 |
|
(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used. |
|||
| Property | Unit of measure | Set value | Actual value (typ.) |
|---|---|---|---|
| Temperature index TI | °C | 200 | 210 |
| Heat shock at 220 °C (no cracks in varnish coat after winding) | mandrel diameter 6x thickness | mandrel diameter 4 x thickness | |
| Solderability | no | no | |
|
(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used. |
|||
| Property | Unit of measure | Set value | Actual value (typ.) |
|---|---|---|---|
| Dielectrical strength at RT | kV | ≥ 2.0 (ball pit) | ≥ 3 (ball pit) |
| High voltage discontiniuties test voltage 2,5 kV | / | ≤ 7 on 100 m | |
| Electrical conductivity | MS/m | 35.5 - 36.2 | ≥ 35.85 |
|
(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used. |
|||
| Property | Set value | Actual value (typ.) |
|---|---|---|
| Pencil hardness (storage in standard solvent ½ h / 60 °C) | min. H | 3H-5H |
| Pencil hardness (storage in alcohol ½ h / 60 °C) | min. H | 3H-5H |
| Resistance to commercial impregnants^(1) | / | yes |
| Resistance to commercial refrigerants^(1) | / | yes |
| Resistance to commercial dry transformer oils^(1) | / | yes |
| Resistance to commercial hydraulic oils^(1) | / | yes |
|
(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used. |
||