SynTherm® – Insulating Materials Teonex® Q5100
Teonex® Q5100 is a flexible, slightly cloudy, biaxially oriented polyethylenenaphthalate (PEN) film.
Compared to PET polyester film, Teonex® Q5100 has optimum properties in every respect.
The increased temperature resistance results in film approval in thermal class F (155 °C). It has a electrical relative temperature index (RTI) of 180 °C and a mechanical RTI of 160 °C according to UL.
Further advantages of Teonex® Q5100 are:
- extremely high dielectric strength
- very good mechanical strength
- high-level of stiffnes
- low water absorption
- easy to laminate
Application
Teonex® Q5100 was specially developed for use in electric motors with increased load as slot insulation, phase insulation and wedges.
Standards
- Class F (155 °C) insulating material
- UL approved, file no. E51743
Delivery forms
Film thicknesses in µm:
- from 12, 16, 25, 38, 50, 75,100, 125, 188, 250
Teonex® Q5100 can be supplied:
- in slit rolls from widths of 6 mm (depending on thickness) and above.
- in rolls up to a width of 1,000 mm
Overall diameter of the slit rolls/ rolls
- approx. 240, 330 or 450 mm.
Feathering:
- depth approx. 1 - 12 mm, distance approx. 1 - 10 mm
- from widths of 10 to 240 mm and thickness of 0.125 mm
Base
Polyethylennaphthalte
Punched parts, bent & formed parts
We offer a wide range of punched and formed parts: Rolls, individual parts unsorted, sorted or stacked, adhesive on one or both sides, non-adhesive, with or without a grip tab.
More about punched parts
Technical data
| Property | Unit of measure | Test method | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Nominal thickness | μm | 12 | 16 | 25 | 38 | 50 | 75 | 100 | 125 | 188 | 250 | |
| Tensile strength longitudinal | MPa | 300 | 330 | 340 | 320 | 290 | 290 | 260 | 260 | 250 | 210 | JIS C2318 |
| Tensile strength transversal | MPa | 330 | 340 | 350 | 320 | 300 | 280 | 280 | 260 | 240 | 190 | JIS C2318 |
| Elongation at break longitudinal | % | 100 | 90 | 100 | 110 | 120 | 100 | 110 | 100 | 110 | 120 | JIS C2318 |
| Elongation at break transversal | % | 90 | 80 | 90 | 110 | 120 | 100 | 100 | 100 | 100 | 110 | JIS C2318 |
| Shrinkage (30 min at 150 °C) longitudinal | % | 0.7 | 1.0 | 1.0 | 0.5 | 0,4 | 0.5 | 0.3 | 0,2 | 0.2 | 0.2 | JIS C2318 |
| Shrinkage (30 min at 150 °C) transversal | % | 0.3 | 0,3 | 0.4 | 0.3 | 0.3 | 0.4 | 0.4 | 0.3 | 0.4 | 0.3 | JIS C2318 |
| Shrinkage at 200 °C longitudinal | % | 2.6 | 2.7 | 2.7 | 1.2 | 0.8 | 1.0 | 0.9 | 1.0 | 1,1 | 0.9 | JIS C2318 |
| Shrinkage at 200 °C transversal | % | 3.5 | 1.7 | 1.9 | 1.3 | 0.8 | 1.0 | 1.1 | 0.8 | 0.7 | 0.7 | JIS C2318 |
| Property | Unit of measure | Test method | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Nominal thickness | μm | 12 | 16 | 25 | 38 | 50 | 75 | 100 | 125 | 188 | 250 | |
| Dielectic strength | kV | 9.6 | 9.6 | 8.1 | 11.2 | 12.7 | 16.2 | 18.0 | 20.7 | 25.0 | 28.7 |